HIC/SSC steel test


SSC test:
In the environment of sulfide corrosion and static tensile stress at the same time under the action of crack according to sulfide stress corrosion cracking (SSC)

 

SSC standards: laboratory tests

NACE TM0177: Laboratory Testing of Metals for Resistance to Sulfide Stress Cracking and Stress Corrosion Cracking in H2S Environments

 

The American association of corrosion engineering standards:

NACE MR0175:Metals for Sulfide Stress Cracking and Stress Corrosion Cracking Resistance in Sour Oilfield Environments

 

NACE MR0175 and NACE TM0177 Applies to all products of corrosion resistant steel, pipe, plate, section steel, spare parts, etc

HIC steel:

HIC (Hydrogen Induced Cracking) is the result of a corrosive reaction between carbon steel and hydrogen sulphide. Wet hydrogen sulphide (H2S) cracking in steel has been a problem in petroleum refining and upstream oil and gas processing since the 1950s. Working conditions where wet H2S prevails are often described as sour service conditions and the term sour gas can be also be used in this context. As more fields rich in H2S are exploited, and this is increasingly the case, the problem is increasingly significant for equipment fabricated in potentially sensitive carbon-manganese (C-Mn) steels.
 
On the chemical composition of carbon steelIn general,HTC Steel requires strict control S,P Content,and to control Mn Content,to improve the performance of steel,you can add some trace elements.

C

Mn

Si

S

P

Nb

V

Nb+V

CE(IIW)

standard

standard

standard

standard

≤0.012

≤0.015

≤0.015

≤0.020

≤0.43

producing HTC Use a lot of clean steel technology in steel, such as low carbon microalloyed technology, Ca Processing technology (change sulfide morphology, the spheroidizing) and Controlled rolling technology of controlled cooling.
 
On the chemical composition of carbon steel forgings:

C

Mn

Si

S+P

CE(IIW)

Steelstandard

Steelstandard

Steelstandard

≤0.015

≤0.45

Carbon steel forgings shall be vacuum degassing and normalizing or quenching and tempering treatment.And 100% UT inspection according to the SA - 388
HIC steel grade

countries Standard grade
China(GB) GB713-2008 Q245R(HIC) Q345R(HIC)
  GB4726-2000 16Mn(HIC)
ASTM A285 A285Gr.A(HIC) A285Gr.B(HIC) A285Gr.C(HIC)
  A442 A442Gr.55(HIC) A442Gr.60(HIC)
  A515 A515Gr.55(HIC) A515Gr.60(HIC) 
A515Gr.65(HIC) A515Gr.70(HIC)
  A516 A516Gr.55(HIC) A516Gr.60(HIC) 
A516Gr.65(HIC) A516Gr.70(HIC)
  A105 A105(HIC)
  A350 A350LF2(HIC)
  A106 A106Gr.B(HIC)
  A333 A333Gr.6(HIC)
DIN EN10025 EN10028-3 S185(HIC) P235GH(HIC)
BS EN10028-2 161GR.400
JIS G3106 SM400A(HIC) SM400B(HIC) SM400C(HIC)
  G3103 SB410(HIC) SB450(HIC) SB480(HIC)
  G3115 SPV235(HIC)
  G3118 SGV410(HIC) SGV450(HIC) SGV480(HIC)

Spot Resource
Corten Steel 09CuPCrNi-A 10mm 787.30$ Corten Steel SPA-H 10mm 573.20$
Corten Steel 09CuPCrNi-A 2.5mm 803.17$ Corten Steel SPA-H 2.5mm 573.20$
Corten Steel 09CuPCrNi-A 2mm 803.17$ Corten Steel SPA-H 2mm 573.20$
Corten Steel 09CuPCrNi-A 3mm 779.37$ Corten Steel SPA-H 6mm 565.08$
Corten Steel 09CuPCrNi-A 4mm 779.37$ Corten Steel SPA-H 8mm 565.08$
Copyright © Henan Seed Steel Metal Materials Co. All rights reserved